    • Electronic properties of GaV4S8: A percolation approach

      I Naik S Hansda A K Rastogi

      More Details Abstract Fulltext PDF

      Two polycrystalline V4-cluster compounds of GaV4S8 were prepared at different annealing temperatures (GaV4S8-1 sintered at 800°C and GaV4S8-2 sintered at 500°C). Their temperature-dependent resistivity and structural phase transformation temperature (45 K for GaV4S8-1 and 43K for GaV4S8-2) are found to be very sensitive to the annealing condition. Above 320 K, activation energy 𝜀3 is calculated to be ∼0.23 eV which decreases to ∼0.18 eV around 300 K in GaV4S8-1 and GaV4S8-2 on cooling. According to percolation theory, the gradual decrease in 𝜀3 below 300 K is expected due to the increase in separation between V4-clusters are significantly different in GaV4S8-1 and GaV4S8-2. This statement is strongly supported by the calculated bandwidth 𝛤 per cluster in GaV4S8 (∼0.342 eV in GaV4S8-1 and ∼0.374 eV in GaV4S8-2). A negative magnetoresistance (MR) is also found around 43 K in GaV4S8-2 at 6.0 T magnetic field associated with structural transition.

  • Pramana – Journal of Physics | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.