Neutron diffraction and Mössbauer measurements have been carried out on the cubic Laves phase intermetallic TbMnFe. The magnetic moment on the transition metal atom is found to be low, 0.2µ_B, at room temperature. This moment is temperature independent down to 10 K. Magnetic moment on the rare earth atom varies from 2.5µ_B at 296 K to 7.27µ_B at 10 K. Mössbauer spectra recorded at 298 K and 78 K have magnetic character but there is a large distribution of hyperfine field values. Both these features arise due to magnetic frustration created in the sample due to the competing ferro and antiferromagnetic interactions between the transition metal atoms.

Nd₂Sn₂O₇ pyrochlores with the substitution of Zr⁴⁺ were prepared by conventional ceramic double sintering technique. The single-phase formation was confirmed by X-ray diffraction and neutron diffraction techniques. Relative intensity calculations for X-ray diffraction analysis were performed for oxygen positional parametersx = 0.331 and 0.375, while Rietveld refinements were employed for neutron diffraction data. The neutron diffraction study revealed that there are only two anion sites with 48f and 8b positions. This indicates that the 8a site, i.e. O(3) sublattice, is completely vacant and the structure is a perfect cubic pyrochlore with space group Fd3m (O_h⁷). From the conductivity measurements, it is observed that the electronic conductivity dominates from room temperature up to about 525 K and forT > 525 K, the oxygen ion conduction dominates the charge transport in these compositions. Complex impedance spectroscopy indicates the existence of grain and grain boundary as two separate elements.