Epitaxial La_1−xPb_xMnO₃ (LPMO) thin films, grown on (100) SrTiO₃ substrates by laser ablation technique at different temperatures between 600 and 850°C, have been characterized for electrical and magnetic properties. The temperature dependence of resistivity showed that the metal-insulator transition temperature (T_MI) decreases with increasing substrate temperature, which has been attributed to decrease in Pb content in the filsm. The YBa₂Cu₃O_x/La_1−xMnO₃ heterostructures, exhibiting both superconductivity and ferromagnetism, have been fabricated.

The layered manganite Nd_2−2xSr_1+2xMn₂O₇, with x varying between 0 and 0.5, has been synthesized using solid-state reaction method. We have found that Nd_2−2xSr_1+2xMn₂O₇ do not form the single-phase layered compound with A₃B₂O₇ structure. Instead, mixtures of various phases, such as, orthorhombic perovskite, i.e., Nd_1−zSr_zMnO₃, layered manganite and unreacted starting compounds, have been obtained. Except for x=0.4, which is found to be an antiferromagnetic insulator, all other x values yielded metal-insulator transition and ferromagnetic ordering.