In the present work, attempts have been made to investigate the modification in particle track etching response of polyallyl diglycol carbonate (PADC) due to impact of 2 MeV electrons. PADC samples pre-irradiated to 1, 10, 20, 40, 60, 80 and 100 Mrad doses of 2 MeV electrons were further exposed to 140 MeV²⁸ Si beam and dose-dependent track registration properties of PADC have been studied. Etch-rate values of the PADC irradiated to 100 Mrad dose electron was found to increase by nearly 4 times that of pristine PADC. The electron irradiation has promoted chain scissioning in PADC, thereby converting the polymer into an easily etchable polymer. Moreover, the etching response and the detection efficiency were found to improve by electron irradiation. Scanning electron microscopy of etched samples further revealed the surface damage in these irradiated PADCs.

The working group on astroparticle and neutrino physics at WHEPP-9 covered a wide range of topics. The main topics were neutrino physics at INO, neutrino astronomy and recent constraints on dark energy coming from cosmological observations of large scale structure and CMB anisotropy.