• Zhanshuang Li

Articles written in Bulletin of Materials Science

• Mesoscale organization of CuO nanoslices: Formation of sphere

The nanocrystalline CuO powders were prepared by precipitation method using Cu(NO$_{3})_{2}$ as copper raw material, water and ethanol as dispersants, and NaOH and ammonia solution as precipitates. The structure, particle size and morphology of resulting CuO powders were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The mechanism of CuO formation was discussed.

• ZnO nanostructured microspheres and grown structures by thermal treatment

Synthesis of flower-shaped ZnO nanostructures composed of ZnO nanosticks was achieved by the solution process using zinc acetate dihydrate, sodium hydroxide and polyethylene glycol-20000 (PEG-20000) at 180°C for 4 h. The diameter of individual nanosticks was about 100 nm. Detailed structure characterizations demonstrate that the synthesized products are wurtzite hexagonal phase, grown along the [001] direction. The infrared (IR) spectrum shows the standard peak of zinc oxide at 571 cm-1. Raman scattering exhibits a sharp and strong 𝐸2 mode at 441 cm-1 which further confirms the good crystal and wurtzite hexagonal phase of the grown nanostructures.

• Study of structural transformations and phases formation upon calcination of Zn–Ni–Al hydrotalcite nanosheets

In this paper, we describe a general process for the synthesis of highly crystalline Zn–Ni–Al hydrotalcitelike materials. The structure and thermal decomposition of the prepared samples are studied by XRD, FT–IR, TG–DSC, SEM, TEM and N2 adsorption/desorption. The morphology of large-sized, porous and hexagonal platelike Zn–Ni–Al hydrotalcite is affected by calcination temperature. BET specific surface area and pore volume are observed to increase with increase of the calcination temperature up to 700°C followed by a further decrease with increasing temperature.