TiC/TiN+TiCN reinforced composite coatings were fabricated on Ti–6Al–4V alloy by laser cladding, which improved surface performance of the substrate. Nano-CeO₂ was able to suppress crystallization and growth of the crystals in the laser-cladded coating to a certain extent.With the addition of proper content of nano-CeO₂, this coating exhibited fine microstructure. In this study, the Al₃Ti+TiC/TiN+nano-CeO₂ laser-cladded coatings were studied by means of X-ray diffraction and scanning electron microscope. The X-ray diffraction results indicated that the Al₃Ti+TiC/TiN+nano-CeO₂ laser-cladded coating consisted of Ti₃Al, TiC, TiN, Ti₂Al₂₀Ce, TiC_0.3N_0.7, Ce(CN)₃ and CeO₂, this phase constituent was beneficial to increase the microhardness and wear resistance of Ti–6Al–6V alloy.

TiC/TiN+TiCN-reinforced composite coatings were fabricated on Ti–6Al–4V alloy by laser cladding, which improved surface performance of the substrate. Nano-CeO₂ was able to suppress crystallization and growth of crystals in the laser-cladded coating to a certain extent. With the addition of proper content of nano-CeO₂, this coating exhibited fine microstructure. In this study, Al₃Ti+TiC/TiN+nano-CeO₂ laser-cladded coatings have been studied by means of X-ray diffraction and scanning electron microscope. X-ray diffraction results indicated that Al₃Ti+TiC/TiN+nano-CeO₂ laser-cladded coating consisted of Ti₃Al, TiC, TiN, Ti₂Al₂₀Ce, TiC_0.3N_0.7, Ce(CN)₃ and CeO₂, this phase constituent was beneficial in increasing microhardness and wear resistance of Ti–6Al–6V alloy.