    • Spray-drying of alumina powder for APS: effect of slurry properties and drying conditions upon particle size and morphology of feedstock

      Bai Yu Yang Jian Feng Lee Soo Wohn Chen Huang Yu Fang Li Zhang Jia

      More Details Abstract Fulltext PDF

      In this paper, effects of variables concerning slurry properties and drying conditions on the particle size and morphology of feedstock were discussed. The results indicated that, the increase of powder loading increased 𝐷50 and volume content but reduced recovery rate slightly. Other variables, such as inlet temperature, showed a maximum on the desired property. The particle size of resulting feedstock increased with the rise of feeding rate of slurry, however, decreased with the increase of atomization pressure based on the premise that atomization pressure was enough to force slurry to form the liquid membrane. For preparation of spherical feedstock, optimized variables were as follows: 60 wt.% powder in slurry, 2 wt.% PVA in slurry, inlet temperature of 60°C, atomization pressure of 13 × 103 KPa and feeding rate of 12 ml min-1. The volume content of feedstocks with 10–45 𝜇m was above 65% and for 𝐷50 it was 15.42 𝜇m. In addition, according to the heat and mass transfer equation, the drying mechanism was established, which was well in agreement with the experimental results.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2022-2023 Indian Academy of Sciences, Bengaluru.