Study on the synthesis and photocatalysis of Ag$_3$PO$_4$ polyhedral microcrystals
TAO GENG SHUANGBIN ZHANG YAO CHEN
The silver phosphate (Ag$_3$PO$_4$) sample was synthesized using Na$_3$PO$_4$, AgNO$_3$ and PEG-10000 as raw materials by the hydrothermal method. Its different morphologies were obtained by changing temperature and surfactant. And its structures and morphology were characterized by X-ray diffraction and field emission scanning electronmicroscopy. The result of the study indicated that after the heat treatment at 150$^{\circ}$C, the as-obtained Ag$_3$PO$_4$ polyhedral microcrystal’s diameter was about 4 $\mu$m. Meanwhile, it showed that using Ag$_3$PO$_4$ polyhedral microcrystals as photocatalysts, the photocatalytic degradation rate of methylene blue in aqueous solution was close to 98.5% after 25 min ofsunlight.
-
-
Bulletin of Materials Science
Volume 45, 2022
All articles
Continuous Article Publishing mode
-
Bulletin of Materials Science | News
-
Dr Shanti Swarup Bhatnagar for Science and Technology
Posted on October 12, 2020Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
Chemical Sciences 2020Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
Physical Sciences 2020 -
Editorial Note on Continuous Article Publication
Posted on July 25, 2019Click here for Editorial Note on CAP Mode
-