Volume 31 Issue 2 April 2008 pp 189-192 Nanomaterials
Poly(vinyl alcohol) (PVA)/CuS composite nanofibres were successfully prepared by electrospinning technique and gas–solid reaction. Scanning electron microscopic (SEM) images showed that the average diameter of PVA/CuS fibres was about 150–200 nm. Transmission electron microscopy (TEM) proved that a majority of CuS nanoparticles with an average diameter of about 15–25 nm are incorporated in the PVA fibres. Xray diffraction (XRD) analyses and electron diffraction pattern also revealed the forming of CuS crystal structure in the PVA fibres.
Volume 34 Issue 3 June 2011 pp 531-533
The ultrafine poly (sodium 4-styrenesulfonate) (NaPSS) fibres have been prepared for the first time by electrospinning. The spinning solutions (NaPSS aqueous solutions) in varied concentrations were studied for electrospinning into ultrafine fibres. The results indicated that the smooth fibre could be formed when the concentration of NaPSS was above 40 wt.%. The morphology of the fibres was shown by scanning electron microscope (SEM). The Fourier transform infrared spectroscopy (FTIR) indicated that the structure of NaPSS did not change after electrospinning.
Volume 42 | Issue 6
Click here for Editorial Note on CAP Mode