Volume 39 Issue 3 June 2016 pp 883-887
TAO ZHU ZANHONG DENG XIAODONG FANG WEIWEI DONG JINGZHEN SHAO RUHUA TAO SHIMAO WANG
Transparent conducting amorphous p-type CuFeO$_2$ (CFO) thin film was prepared by radio-frequency (RF) magnetron sputtering method at room temperature using polycrystalline CuFeO$_2$ target. Amorphous structureof as-deposited film was confirmed by XRD. XPS analysis convinced that the chemical state of Cu$^{+}$ and Fe$^{3+}$ in the film, and the chemical composition of the thin films is close to the stoichiometry of CuFeO$^2$. Surface morphology of the film was analysed by SEM studies. p-type nature and concentration of carriers was investigated by Hall effect measurement. The p–n heterojunction in the structure of Al/n-Si/p-CuFeO$_2$/Al showed good rectifying behaviour with a forward and reverse currents ratio of 555 at 2 V. The turn-on voltage and reverse leakage current values were found to be 0.9 V and 4 $\mu$A at $−$2 V. Further, the conduction mechanism of forward bias voltage was controlled by thermionic emission (TE) and trap-space charge limited current (TCLC) mechanisms.
-
-
Bulletin of Materials Science
Volume 46, 2023
All articles
Continuous Article Publishing mode
-
Bulletin of Materials Science | News
-
Dr Shanti Swarup Bhatnagar for Science and Technology
Posted on October 12, 2020Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
Chemical Sciences 2020Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
Physical Sciences 2020 -
Editorial Note on Continuous Article Publication
Posted on July 25, 2019Click here for Editorial Note on CAP Mode
-