Volume 39 Issue 5 September 2016 pp 1259-1262
TAOTAO AI QI YU WENHU LI XIANGYU ZOU ZHIFENG DENG XINQIANG YUAN
In situ Ti$_2$AlC/TiAl composite was fabricated by hot-pressing method via the reaction system of Ti$_3$AlC$_2$ and Ti-Al pre-alloyed powders at low temperature of 1150$^{\circ}$C. The composite mainly consisted of TiAl, Ti$_3$Al and Ti$_2$AlC phases. Fine Ti$_2$AlC particles were homogeneously distributed and dispersed in the matrix. Ti$_2$AlC played the significant role of deflecting and blunting the cracks and contributed to improve the mechanical properties of the composite. The Vickers hardness, flexural strength and fracture toughness were 6.2 GPa, $993.9\pm 50.8$ MPa and $6.7\pm 0.3$ MPa m$^{1/2}$, respectively.
-
-
Bulletin of Materials Science
Volume 44, 2021
All articles
Continuous Article Publishing mode
-
Bulletin of Materials Science | News
-
Dr Shanti Swarup Bhatnagar for Science and Technology
Posted on October 12, 2020Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
Chemical Sciences 2020Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
Physical Sciences 2020 -
Editorial Note on Continuous Article Publication
Posted on July 25, 2019Click here for Editorial Note on CAP Mode
-