Volume 40 Issue 1 February 2017 pp 233-238
Dense-plasma-driven ultrafast formation of FePt organization on silicon substrate
ROHIT MEDWAL NEERU SEHDEV WANG YING R S RAWAT S ANNAPOORNI
This article demonstrates the removal of organic capping and promotion of long-range 2D organization of chemically synthesized FePt nanoparticles dispersed on Si$\langle 100\rangle$ substrate by means of pulsed H+ energetic ion irradiation using a dense plasma focus (DPF) device. The irradiation of energetic H$^+$ ions on FePt nanoparticles clearly resulted in enhanced structural and magnetic behaviour of the FePt nanoparticles as a function ofplasma focused irradiation shots. Transmission electron microscopy (TEM)/scanning electron microscopy (SEM) images of the FePt nanoparticles clearly show a marked enhancement in average particle size from 2.5 nm for nonirradiated sample to about 28nm for four plasma focus shots irradiation. The gradual removal of organic capping over chemically synthesized FePt nanoparticles with increasing plasma focus shots exposure is confirmed usingRaman spectroscopy. A uniform 2D organization of bimetallic FePt nanoparticles over 1 cm $\times$ 1 cm silicon substrate is obtained with three plasma focus shots with better magnetic properties as compared with plasma-untreated FePtnanoparticles.
Volume 45, 2022
All articles
Continuous Article Publishing mode
Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
Chemical Sciences 2020
Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
Physical Sciences 2020
Click here for Editorial Note on CAP Mode
© 2021-2022 Indian Academy of Sciences, Bengaluru.