    • Preparation and characterization of solid-state sintered aluminum-doped zinc oxide with different alumina contents

      Yu-Hsien Chou J L H Chau W L Wang C S Chen S H Wang C C Yang

      More Details Abstract Fulltext PDF

      Aluminum-doped zinc oxide (AZO) ceramics with 0−2.5 wt.% alumina (Al2O3) content were prepared using a solid-state reaction technique. It was found that AZO grains became finer in size and more irregular in shape than undoped ZnO as the Al2O3 content increased. Addition of Al2O3 dopant caused the formation of phase transformation stacking faults in ZnO grains. The second phase, ZnAl2O4 spinel, was observed at the grain boundaries and triple junctions, and inside the grains. In this study, a 3-inch circular Al2O3 (2 wt.%)-doped ZnO ceramic target sintered at 1500°C for 6 h has a relative density of 99.8% with a resistivity of 1.8 × 10-3 𝛺-cm. The AZO film exhibits optical transparency of 90.3% in the visible region and shows an electrical resistivity of 2.5 × 10-3 𝛺 -cm.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.