The oxygen-deficient phase of the highT_c superconductor, YBa₂Cu₃O₇, was oxygen-enriched using the fluidization technique to give good superconducting properties. The normal method of oxygen treatment at 900°C for 24 h and at 600°C for 24 h has been reduced to just one treatment at 600°C for 12 h by the fluidization technique to achieve almost the same strength of superconducting signal for the YBa₂Cu₃O₇ powder, which establishes the attractiveness of the latter route for the large-scale preparation of superconducting material. The particle sizes were in the range 0–90, 90–180 and 180–420 µm. The fluidized particles were crystalline with orthorhombic distortion.T_c^onset, estimated using the a.c. magnetic susceptibility method, was 91·3 K. The volume fraction of superconducting material in the product was 83·7–85·3%, one of the highest values reported so far for YBa₂Cu₃O₇.