Volume 38 Issue 4 August 2015 pp 951-955
TiZrN coating was deposited on 316L stainless steel (SS) by the reactive magnetron co-sputtering technique. Cubic phase of TiZrN with uniform surface morphology was observed by X-ray diffraction and atomic force microscopy. Bacterial adhesion, haemocompatibility and corrosion behaviour of TiZrN coating were examined in order to evaluate the coating’s compatibility for ideal implant. Results revealed that TiZrN coatings exhibited less bacterial attachment against
Volume 39 Issue 2 April 2016 pp 385-389
Biogenic calcium carbonate/phosphate were isolated and characterized from oral bacteria (CPOB). The crystalline nature and morphology of calcium carbonate/phosphate were characterized by X-ray diffraction (XRD)and field emission scanning electron microscopy (FESEM), respectively. XRD analysis revealed the cubic phase of YSZ coating as well as biogenic calcium carbonate (rhombohedral) and calcium phosphate oxide (hexagonal) wasobserved from CPOB. FESEM confirmed the extracellular synthesis of calcium compounds. Bacterial adhesion result reveals that YSZ coating drastically reduce bacterial invasion than titanium substrate.
Volume 42 | Issue 6
Click here for Editorial Note on CAP Mode