Volume 35 Issue 3 June 2012 pp 327-331
Influence of pH on ZnO nanocrystalline thin films prepared by sol–gel dip coating method
K Sivakumar V Senthil Kumar N Muthukumarasamy M Thambidurai T S Senthil
ZnO nanocrystalline thin films have been prepared on glass substrates by sol–gel dip coating method. ZnO thin films have been coated at room temperature and at four different pH values of 4, 6, 8 and 10. The X-ray diffraction pattern showed that ZnO nanocrystalline thin films are of hexagonal structure and the grain size was found to be in the range of 25–45 nm. Scanning electron microscopic images show that the surface morphology improves with increase of pH values. TEM analysis reveals formation of ZnO nanocrystalline with an average grain size of 44 nm. The compositional analysis results show that Zn and O are present in the sample. Optical band studies show that the films are highly transparent and exhibit a direct bandgap. The bandgap has been found to lie in the range of 3.14–3.32 eV depending on pH suggesting the formation of ZnO nanocrystalline thin films.
-
-
Bulletin of Materials Science
Volume 46, 2023
All articles
Continuous Article Publishing mode
-
Bulletin of Materials Science | News
-
Dr Shanti Swarup Bhatnagar for Science and Technology
Posted on October 12, 2020Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
Chemical Sciences 2020Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
Physical Sciences 2020 -
Editorial Note on Continuous Article Publication
Posted on July 25, 2019Click here for Editorial Note on CAP Mode
-