    • Interface behaviour and electrical performance of ruthenium Schottky contact on 4H-SiC after argon annealing

      Kinnock V munthali Chris Theron F Danie Auret Sergio M M Coelho

      More Details Abstract Fulltext PDF

      Rutherford backscattering spectrometry (RBS) analysis, carried out at various annealing temperatures, of a thin film of ruthenium on n-type four-hexagonal silicon carbide (4H-SiC) showed the evidence of ruthenium oxidation, ruthenium silicide formation and diffusion of ruthenium into silicon carbide starting from an annealing temperature of 400° C. Ruthenium oxidation was more pronounced, and ruthenium and silicon interdiffusion was very deep after annealing at 800° C. Raman analysis of some samples also showed ruthenium silicide formation and oxidation. The Schottky barrier diodes showed very good linear capacitance–voltage characteristics and excellent forward current–voltage characteristics, despite the occurrence of the chemical reactions and interdiffusion of ruthenium and silicon at ruthenium–silicon–carbide interface, up to an annealing temperature of 800° C.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.