• SOURAV GHOSH

      Articles written in Bulletin of Materials Science

    • Investigating the role of amides on the textural and optical properties of mesoporous-nanostructured $\theta$-Al$_2$O3

      SOURAV GHOSH SUKANYA KUNDU RITUPARNA DAS MILAN KANTI NASKAR

      More Details Abstract Fulltext PDF

      Mesoporous-nanostructured $\theta$-Al$_2$O$_3$ was synthesized by an autoclaving technique using different amidesi.e., formamide (F), dimethyl formamide (DMF) and diethyl formamide (DEF) at 150$^{\circ}$C/24 h followed by calcinationat 1000$^{\circ}$C. Crystallization and structural behaviour of the as-synthesized materials were characterized by X-raydiffraction and Fourier transform infrared spectroscopy. The porosity study was carried out by N2 adsorption–desorption(BET) technique. Microstructural features were measured by transmission electron microscopy (TEM). The amidebasedsolvents played a deliberate role in microstructural and textural features of $\theta$-Al$_2$O$_3$. The DMF-based solventshowed an enhanced surface area of 158 m$2^$ g$^{−1}$. The as-prepared $\theta$-Al$_2$O$_3$ rendered a nano-sheet, nano-rod and nano-flake like morphology for F, DMF and DEF derived products, respectively. From the UV–Vis spectroscopic measurement, the estimated band-gap of $\theta$-Al$_2$O$_3$ was found to be 5.16–5.40 eV. Photoluminescence investigation further revealed blue emission particularly for excitation at a wavelength of 252 nm. A DMF-derived sample rendered thelowest band gap due to its smaller crystallite size and higher surface area compared to that of F- and DEF-derivedsamples.

    • Mesoporous CuO nanostructures for low-temperature CO oxidation

      SOURAV GHOSH SUKANYA KUNDU MILAN KANTI NASKAR

      More Details Abstract Fulltext PDF

      Preparation of CuO nanostructure was reported by oxalic acid-assisted wet-chemical method in aqueous medium. As-prepared sample was identified as C$_2$CuO$_4$.$n$H$_2$O, which was further transformed into CuO after heat treatment. To enhance the textural property, CTAB was employed as soft-templating agent. DTA–TGA characterization was performed to investigate the thermal stability of as-prepared C$_2$CuO$_4$.$n$H$_2$O sample, whereas Raman and XPS measurements confirmed the presence of CuO. FESEM and TEM studies revealed porous architecture with shelled interior for CuO sample. The formation of porous network could be demonstrated by oxidative decomposition of C$_2$CuO$_4$.$n$H$_2$O due to high temperature calcination. The BET surface area and pore volume were found to be 51 m$^2$ g$^{-1}$ and 0.4492 cc g$^{-1}$, respectively. The catalytic activity of sample was investigated for CO oxidation and achived $T_{50}$ and $T_{100}$ at 133 and 175°C, respectively, which were further compared with commercialized CuO sample and previously reported data.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.