• SHOMAILA KHANAM

      Articles written in Bulletin of Materials Science

    • Decolourization of rhodamine B and methylene blue dyes in the presence of bismuth tungstates: a detailed investigation on the effect of grain size

      SHOMAILA KHANAM SANJEEB KUMAR ROUT

      More Details Abstract Fulltext PDF

      Solid-state reaction method was opted for the preparation of bismuth tungstates (Bi$_2$WO$_6$) in the stoichiometric ratio. The structural characterization related that the material has got orthorhombic symmetry. The high-energy ball milling did not show any structural change, but a reduction in grain size was observed from 100 to 34 nm after 5 h. The higher activity for the decolourization of rhodamine B (RHB) and methylene blue (MB) in the presence of UV light has been studied by employing Bi$_2$WO$_6$ as a catalyst. The dye degradation was observed by a decrease in the absorption spectrum and decolourization in the presence of UV irradiation. The degradation efficiency was found to be dependent on the size of the catalyst added in the dye solution, which may be due to increased surface area that increased the number ofactive sites for the reaction. The degradation efficiency of the unmilled and 5-h ball milled (Bi$_2$WO$_6$) catalyst was observed to be 32 and 90% in RHB, respectively. While in MB, 24 and 49% degradation efficiency was achieved byunmilled and 5-h ball milled (Bi$_2$WO$_6$) catalyst. The degradation rate coefficient was found to be in the decreasing order of RHB>MB, which pursued the first-order kinetic mechanism. Therefore, Bi2WO6 can act as a catalyst for the treatment of noxious and imperishable organic pollutants in water.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.