    • Nanoscale grain growth behaviour of CoAl intermetallic synthesized by mechanical alloying

      S N Hosseini M H Enayati F Karimzadeh

      More Details Abstract Fulltext PDF

      Grain growth behaviour of the nanocrystalline CoAl intermetallic compound synthesized by mechanical alloying has been studied by isothermal annealing at different temperatures and durations. X-ray diffraction method was employed to investigate structural evolutions during mechanical alloying and annealing processes. The disordered CoAl phase with the grain size of about 6 nm was formed via a gradual reaction during mechanical alloying. The results of isothermal annealing showed that the grain growth behaviour can be explained by the parabolic grain growth law. The grains were at nanometric scale after isothermal annealing up to 0.7 𝑇m. The grain growth exponent remained constant above 873 K indicating that grain growth mechanism does not change at high temperatures. The calculated activation energy indicated that the grain growth mechanism in the disordered CoAl phase at high temperatures was diffusing Co and Al atoms in two separate sublattices. Furthermore, an equation has been suggested to describe the grain growth kinetics of nanocrystalline CoAl under isothermal annealing at temperatures above 873 K (𝑇/𝑇m ≥ 0.5).

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.