Volume 38 Issue 6 October 2015 pp 1527-1531
The polycrystalline sample of LiBaPO4 : Tb3+ (LBPT) was successfully synthesized by solution combustion synthesis and studied for its luminescence characteristics. The thermoluminescence (TL) glow curve of LBPT material consists of two peaks at 204.54 and 251.21°C. The optimum concentration was 0.005 mol to obtain the higher TL intensity compared to commercial TLD-100 phosphor. The peak shape method was used to calculate kinetic parameter (activation energy and frequency factor). In CW-OSL mode its sensitivity for beta exposure was found to be 50% compared to commercially available 𝛼-Al2O3 : C and 40% than LMP (BARC), and photoluminescence spectrum of LBPT shows green emission when excited with 225 nm UV source.