    • Preparation and thermomechanical properties of stir cast Al–2Mg–11TiO2 (rutile) composite

      S K Chaudhury A K Singh C S S Sivaramakrishnan S C Panigrahi

      More Details Abstract Fulltext PDF

      Al–2Mg–11TiO2 composite was successfully prepared by the conventional vortex method. The macrostructural observation revealed columnar structure with rutile particles being distributed throughout the matrix in the form of agglomerates. Microstructural observation showed the presence of micro voids in the particle-enriched zone. Electrical resistivity measurement showed a phase transformation at 360°C, which was consistent during DSC studies due to the precipitation of TiAl3 phase. As-cast composite was both hot rolled and cold rolled successfully to 50 and 40% reduction, respectively. The mechanical properties of the thermomechanically-worked composite were studied. From fractographic analysis, it was clear that the crack had nucleated at the particle/matrix interface and propagated through the matrix by microvoid coalescence. Ultimate tensile strength of cold worked composite was found to be better than the hot worked material.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2023-2024 Indian Academy of Sciences, Bengaluru.