Volume 25 Issue 6 November 2002 pp 557-560
Precursor sol for sol–gel silica layer was prepared from the starting material, tetraethylorthosilicate (TEOS). The sol was deposited onto borosilicate crown (BSC) glass by the spinning technique (rpm 2500). The gel layer thus formed transformed to oxide layer on heating to 450°C for ∼ 30 min. The physical thicknessand the refractive index of the layer were measured ellipsometrically (Rudolph Auto EL II) at 632.8 nm. About 10 × 10 mm surface area of the silica layer was chosen for evaluation of thickness and refractive index values at different points (121 nos.) with 1 mm gap between two points. Those data were utilized in the Autolisp programme for 3-D mapping. Radial distribution of the evaluated values was also displayed.