    • Surface modification on PMMA : PVDF polyblend: hardening under chemical environment

      R Bajpai V Mishra Pragyesh Agrawal S C Datt

      More Details Abstract Fulltext PDF

      The influence of chemical environment on polymers include the surface alteration as well as other deep modifications in surface layers. The surface hardening, as an effect of organic liquids on poly(methyl methacrylate): poly(vinylidene fluoride) (PMMA: PVDF), which is one of the few known miscible blends, has been detected using microhardness testing. Organic liquids like acetone, toluene, xylene and benzene were introduced on the surface of blend specimens for different durations. Vickers microhardness (𝐻v) was measured for treated and untreated specimens. The study reveals both hardening and plasticization of specimens at different exposure times. The degree of surface hardening is maximum under acetone treatment. All the specimens exhibit surface hardening at an exposure time of 1 h with all the four liquids. This feature is prominent with longer exposures for specimens with increasing content of PVDF. However, the degree of hardening decreases with the time of exposure in the respective environments. In general, acetone and toluene impart surface hardening, whereas, xylene and benzene soften the specimen. PMMA: PVDF (83 : 17) blend exhibits surface hardening under all the four treatments when compared with the respective untreated specimens.

    • Development of hardened PVF : PMMA polyblend: effect of gamma and electron irradiation

      R Bajpai N B Dhagat R Katare Pragyesh Agrawal S C Datt

      More Details Abstract Fulltext PDF

      Specimens of poly(vinyl formal) (PVF) : poly(methyl methacrylate) (PMMA) polyblends with different weight percentage ratios were subjected to gamma irradiation (1 to 50 Mrad) and electron irradiation (1 to 20 Mrad). The effect of irradiation on the strength of the blend specimens was studied by measuring the surface microhardness using a Vickers microhardness tester attached to a Carl Zeiss NU 2 Universal research microscope. Significant changes were observed in the Vickers microhardness number, $H_v$. The $H_v$ values of gamma irradiated specimens are found to be higher than the unirradiated specimens indicating an occurrence of radiational crosslinking. The maximum value of $H_v$ is obtained at the gamma radiation dose of 15 Mrad. In case of electron irradiation the radiational crosslinking is found to take place for the blend specimens having lower wt% content of PMMA (0 and 1 wt%) in PVF matrix. On the other hand degradation of polymeric system is observed for the blends having PMMA content more than 1 wt%. The maximum value of $H_v$ is obtained for all the blend specimens at the electron irradiation dose of 8 Mrad. The degree of crosslinking in polyblends due to gamma irradiation is found to be more than electron irradiation. The scissioning mechanism is found to predominate in the polyblend system in case of electron irradiation.

  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.