    • Interfacial microstructure and strength of diffusion brazed joint between Al2O3–TiC and 9Cr1MoV steel

      Wang Juan Li Yajiang S A Gerasimov

      More Details Abstract Fulltext PDF

      Joining of composite, Al2O3–TiC, with heat-resistant 9Cr1MoV steel, was carried out by diffusion brazing technology, using a combination of Ti, Cu and Ti as multi-interlayer. The interfacial strength was measured by shear testing and the result was explained by the fracture morphology. Microstructural characterization of the Al2O3–TiC/9Cr1MoV joint was investigated by X-ray diffraction (XRD) and scanning electron microscope (SEM) with energy-dispersion spectroscopy (EDS). The results indicate that a Al2O3–TiC/9Cr1MoV joint with a shear strength of 122 MPa can be obtained by controlling heating temperature at 1130°C for 60 min with a pressure of 12 MPa. Multi-interlayer Ti/Cu/Ti was fused fully and diffusion occurred to produce interfacial layer between Al2O3–TiC and 9Cr1MoV steel. The total thickness of the interfacial layer is about 100 𝜇m and Ti3AlC2, TiC, Cu and Fe2Ti are found to occur in the interface layer.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.