    • Combustion synthesis of Eu2+ and Dy3+ activated Sr3(VO4)2 phosphor for LEDs

      Roshani Singh S J Dhoble

      More Details Abstract Fulltext PDF

      Combustion synthesis and photoluminescence (PL) characterization of Sr3(VO4)2:Eu,Dy phosphors are presented in this paper. PL emission of Sr3(VO4)2:Eu phosphor shows green broad emission band centring at 511 nm and a red sharp band at 614 nm by excitation wavelength of 342 nm. The PL emission spectrum of Sr3(VO4)2:Dy phosphor exhibits an intense blue emission peak at 479 nm, yellow broad band centring at 573 nm and red band at 644 nm by the excitation wavelength of 426 nm in near visible blue region. The excitation wavelength of Eu (342 nm) and Dy (426 nm) activated Sr3(VO4)2 phosphor are well matched with the excitation of near UV excited solid state lighting and blue chip excitation of light emitting diodes, respectively. The effect of Eu2+ and Eu3+ ions concentration on the emission intensity of Sr3(VO4)2 was also investigated. The Sr3(VO4)2:Eu is a potential green and red emitting phosphor as well as Sr3(VO4)2:Dy is blue and yellow emitting phosphor for solid state lighting i.e. white LEDs. The XRD and SEM characteristics of Sr3(VO4)2 materials was also reported in this paper.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.