Volume 38 Issue 3 June 2015 pp 673-678
Silica-calcium zirconate nanocomposite, studying its thermal and electrical properties
Neda Kermani Maryam Kargar Razi Seyed Saeed Mirzaee Reza Tayebee
Silica–calcium zirconate nanocomposite was prepared in a two-step procedure. First, nanocalcium zirconate was synthesized by the modified sol–gel method; then, silica was added to the prepared sol and the resulting product was calcined at 700–1000° C. Dilatometric measurements were performed to determine the coefficient of thermal expansion (𝑘𝛼). It was concluded that 𝑘𝛼 was decreased from 15.96 × 10−6 to 10.26 × 10−6 1° C−1 with the increase in calcium zirconate/silica ratio. Moreover, studies on the dielectric properties and calcination temperature showed that the dielectric constant (𝜀r) was increased from 3.9 to 5.7.
-
-
Bulletin of Materials Science
Volume 45, 2022
All articles
Continuous Article Publishing mode
-
Bulletin of Materials Science | News
-
Dr Shanti Swarup Bhatnagar for Science and Technology
Posted on October 12, 2020Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
Chemical Sciences 2020Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
Physical Sciences 2020 -
Editorial Note on Continuous Article Publication
Posted on July 25, 2019Click here for Editorial Note on CAP Mode
-