    • Structural, optical and electrical properties of ZnO thin films prepared by spray pyrolysis: Effect of precursor concentration

      F Zahedi R S Dariani S M Rozati

      More Details Abstract Fulltext PDF

      ZnO thin films have been prepared using zinc acetate precursor by spray pyrolytic decomposition of zinc acetate on glass substrates at 450 °C. Effect of precursor concentration on structural and optical properties has been investigated. ZnO films are polycrystalline with (002) plane as preferential orientation. The optical transmission spectrum shows that transmission increases with decrease in the concentration and the maximum transmission in visible region is about 95% for ZnO films prepared with 0.1 M. The direct band-gap value decreases from 3.37 to 3.19 eV, when the precursor concentration increases from 0.1 to 0.4 M. Photoluminescence spectra at room temperature show an ultraviolet (UV) emission at 3.26 eV and two visible emissions at 2.82 and 2.38 eV. Lowest resistivity is obtained at 2.09 𝛺 cm for 0.3 M. The current–voltage characteristic of the ZnO thin films were measured in dark and under UV illumination. The values of photocurrent and photoresponsivity at 5 V are increased with increase in precursor concentration and reaches to maximum value of 1148 𝜇A and 0.287 A/W, respectively which is correlated to structural properties of ZnO thin films.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.