Volume 29 Issue 2 April 2006 pp 165-168 Thin Films
Structural, electrical and optical characteristics of CdTe thin films prepared by a chemical deposition method, successive ionic layer adsorption and reaction (SILAR), are described. For deposition of CdTe thin films, cadmium acetate was used as cationic and sodium tellurite as anionic precursor in aqueous medium. In this process hydrazine hydrate is used as reducing agent and NH4OH as the catalytic for the decomposition of hydrazine. By conducting several trials optimization of the adsorption, reaction and rinsing time duration for CdTe thin film deposition was done. In this paper the structural, optical and electrical properties of CdTe film are reported. The XRD pattern shows that films are nanocrystalline in nature. The resistivity is found to be of the order of 4.11 × 103 𝛺-cm at 523 K temperature with an activation energy of ∼ 0.2 eV. The optical absorption studies show that films have direct band gap (1.41 eV).
Volume 29 Issue 4 August 2006 pp 413-416 Thin Films
This paper describes the results of thermally stimulated discharge conductivity study of activated charcoal–polyvinyl chloride (PVC) thin film thermoelectrets. TSDC has been carried out in the temperature range 308–400°K and at four different polarizing fields. Results are discussed on the basis of mobility of activated charcoal and polyvinyl chloride chains.
Volume 30 Issue 2 April 2007 pp 163-166 Polymers
The electrical conductivity of naphthalene doped polystyrene (PS) films (≈ 61.58 𝜇m thick) was studied as a function of dopant concentration and temperature. The formation of charge transfer (CT) complexes and strong concentration dependence of carrier mobility point out that the current carriers are transported through doped polymer system via hopping among sites associated with the dopant molecules. The activation energy, 𝐸a, was calculated from the graph of log𝜎vs 103/𝑇 plot within low and high temperature regions.
Volume 43, 2020
Continuous Article Publishing mode
Click here for Editorial Note on CAP Mode