    • Bi$^{3+}$-doped Ba$_2$Y$_{1-x}$Lu$_x$NbO$_6$:Bi$^{3+}$ ($0 \leq x \leq 1.0$) solid solution phosphors: tunable photoluminescence and application for white LEDs

      CHANGSHUN ZHOU CHENHUI JIANG JUN ZHAO PEIMIN ZHAN XUFANG TANG DINGFENG JIN XINXING WANG

      More Details Abstract Fulltext PDF

      In this work, we use the conventional high temperature solid-state reaction to prepare Bi$^{3+}$-doped Ba$_2$Y$_{1-x}$Lu$_x$NbO$_6$:Bi$^{3+}$ ($0 \leq x \leq 1.0$) solid solution phosphors. To study the Lu$^{3+}$ content-dependent structural evolution and photoluminescence (PL) properties of the samples, the powder X-ray diffraction (pXRD), density functional theoretical (DFT) calculations, UV–visible diffuse reflectance and PL spectra are used. We find that all the phosphors are double-perovskite structural phase with a cubic space group of Fm$\bar{3}$m, and the XRD positions shift to higher diffraction angle with the increase in Lu$^{3+}$ content. The emission positions of the samples tune from 447 to 493 nm, which are due to the crystal field modulation around the Bi3? ion. Among the obtained samples, the Ba$_2$Y$_{0.7}$Lu$_{0.3}$NbO$_6$:Bi$^{3+}$ shows the bestquantum efficiency (QE) of 57%. By using the optimal Ba$_2$Y$_{0.7}$Lu$_{0.3}$NbO$_6$:Bi$^{3+}$ solid solution phosphor, the red-emitting CaAlSiN:Eu$^{2+}$ phosphor, and a commercial 365 nm UV LED chip, we have fabricated a white LED device with the CIE coordinates at (0.378, 0.373), colour temperature (CT) of 3513 K, colour rendering index (CRI) of 67.1 and luminous efficiency of 39 lm W$^{-1}$.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.