    • Physical and chemical response of 70 MeV carbon ion irradiated Kapton-H polymer

      H S Virk P S Chandi A K Srivastava

      More Details Abstract Fulltext PDF

      Physical and chemical responses of 70 MeV carbon ion irradiated Kapton-H polymer were studied by using UV-visible, FTIR and XRD techniques. The ion fluences ranging from 9.3 × 1011–9 × 1013 ions cm–2 were used. Recorded UV-visible spectra clearly showed a decrease in absorption initially with fluence, but for the higher fluences it showed a recovery characteristic. A decrease in band-gap energy of 0.07 eV was observed. The FTIR analysis indicated the high resistance to radiation induced degradation of polymer. The diffraction pattern of Kapton-H indicates that this polymer is semi-crystalline in its nature. In case of irradiated one, there was an average increase of crystallite size by 20%, but diffuse pattern indicates that there was a decrease in crystallinity, which may be attributed to the formation of complex structure induced by the cross-linking of the polymeric chains.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.