Volume 28 Issue 6 October 2005 pp 609-615 Thin Films
Structural morphology of amorphous conducting carbon film
P N Vishwakarma V Prasad S V Subramanyam V Ganesan
Amorphous conducting carbon films deposited over quartz substrates were analysed using X-ray diffraction and AFM technique. X-ray diffraction data reveal disorder and roughness in the plane of graphene sheet as compared to that of graphite. This roughness increases with decrease in preparation temperature. The AFM data shows surface roughness of carbon films depending on preparation temperatures. The surface roughness increases with decrease in preparation temperature. Also some nucleating islands were seen on the samples prepared at 900°C, which are not present on the films prepared at 700°C. Detailed analysis of these islands reveals distorted graphitic lattice arrangement. So we believe these islands to be nucleating graphitic. Power spectrum density (PSD) analysis of the carbon surface indicates a transition from the nonlinear growth mode to linear surface-diffusion dominated growth mode resulting in a relatively smoother surface as one moves from low preparation temperature to high preparation temperature. The amorphous carbon films deposited over a rough quartz substrate reveal nucleating diamond like structures. The density of these nucleating diamond like structures was found to be independent of substrate temperature (700–900°C).
-
-
Bulletin of Materials Science
Volume 46, 2023
All articles
Continuous Article Publishing mode
-
Bulletin of Materials Science | News
-
Dr Shanti Swarup Bhatnagar for Science and Technology
Posted on October 12, 2020Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
Chemical Sciences 2020Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
Physical Sciences 2020 -
Editorial Note on Continuous Article Publication
Posted on July 25, 2019Click here for Editorial Note on CAP Mode
-