    • Microstructural and densification study of natural Indian magnesite in presence of zirconia additive

      Kaberi Das Saswata Mukherjee P K Maiti P G Pal

      More Details Abstract Fulltext PDF

      The sintering and microstructural evaluation of Indian magnesite was carried out in presence of zirconia. Zirconia in monoclinic form was added in the range 3–6 wt% with respect to raw magnesite and the sintering temperature selected were 1500–1600°C for 2 h. The main impurities present in the magnesite were Fe2O3, CaO, SiO2. The natural crystalline magnesite could be sintered with bulk density of 3.38 g/cc (A.P. 1.54%) at 1550°C/2 h. But the higher bulk density (3.50 g/cc) and minimum apparent porosity (A.P. 0.25%) was attained at 1550°C/2 h with the 3 wt% zirconia additive. On firing magnesite with zirconia as additive, a crystalline phase, magnesio-zirconate, was identified at the triple point regions of the direct bonded periclase grains. The morphology of the periclase grains were changed from subrounded/rounded to angular shaped in presence of zirconia as additive.

  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.