Volume 38 Issue 5 September 2015 pp 1465-1472
Using nickel, zinc and ferric nitrates, and glycine in a fuel-rich composition, Ni1–𝑥Zn𝑥Fe2O4 nanoparticles were prepared by a simple low-temperature auto-combustion method without further sintering at high temperatures. The auto-combusted powders obtained were characterized by X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscopy, energy-dispersive X-ray (EDAX) analysis and vibrating scanning magnetometer measurements. XRD confirms the formation of pure nanocrystalline spinel phases with an average diameter of about 55 nm. Raman spectra show tetrahedral and octahedral sites in the structure of Ni1–𝑥Zn𝑥Fe2O4 and also imply the doping of Zn2+ and displacement of Fe3+ ions from the tetrahedral site. EDAX showed that the samples were close to the nominal compositions. The magnetic measurement shows that the saturation magnetization and remanence magnetization decreases with the increase in the zinc content.
Volume 43, 2020
Continuous Article Publishing mode
Click here for Editorial Note on CAP Mode