    • Effect of titania on fired characteristics of triaxial porcelain

      Sunipa Bhattacharyya Swapan Kumar Das Nirendra Krishna Mitra

      More Details Abstract Fulltext PDF

      Titania was progressively added in the range 3–9 wt% into a triaxial porcelain body consisting of clay, quartz and feldspar. The composed bodies were heated at five different temperatures in the range 1200–1400°C and their fired properties as well as phases evolved were studied. The results revealed that beyond 1300°C, formation of more liquid phases caused bloating in samples which led to generation of pores. This effect is more pronounced in TiO2 containing samples. In the present system, 1300°C appeared to be the optimum temperature at which porosity was almost negligible and strength was maximum (45 MPa), particularly in presence of TiO2. From the results of XRD studies, it was revealed that quartz content primarily decreased with increase in TiO2 content due to excess glass formation and its subsequent dissolution. Mullite content increased with increase in TiO2 content. No significant effect was observed beyond 6 wt% addition. Microstructure primarily showed the presence of quartz grain and cluster of smaller sized primary mullite crystals in both the samples without and with TiO2. Very few secondary mullite crystals were also observed. SEM picture of sample containing 9 wt% TiO2 showed some grain boundary crack due to cooling stress generated in the glassy phase. The drastic reduction of residual strength after 8 cycles of heating at 800°C and cooling particularly in TiO2 containing samples suggests controlled heat treatment of the vitrified samples necessary to promote secondary crystallization process for the enhancement of strength. Attempts have also been made to correlate the constitutional parameters with the properties.

    • Titania doped triaxial porcelain: Enhancement of strength by controlled heat treatment

      Sunipa Bhattacharyya Swapan Kumar Das Kausik Dana Nirendra Krishna Mitra

      More Details Abstract Fulltext PDF

      Titania doped vitrified triaxial porcelain samples were subjected to controlled heat treatment at different temperatures of 600, 800 and 1000°C with a specific heating schedule. The results revealed that flexural strength of 800°C heat treated sample was significantly enhanced to 60 MPa from its original value of 40 MPa. XRD pattern revealed the formation of mullite in the system both before and after heat treatment and the differences in their growth was ascertained through SEM analysis. The present heat treatment process may be useful to produce high strength porcelain body from a common triaxial system.

  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.