Volume 35 Issue 2 April 2012 pp 253-258
High-resolution X-ray diffraction technique, employing a three-crystal monochromator–collimator combination is used to study the irradiation induced defects in flux grown Sr-hexaferrite crystals irradiated with 50 MeV Li3+ ion beams at room temperature with a fluence value of 1 × 1014 ions/cm2. The diffraction curves of the irradiated crystals suggest the possibility of creation of low angle grain boundaries and other point/clusters of defects causing amorphization in the irradiated crystals. The perfection of the irradiated and unirradiated (0001) cleaved surfaces of the crystals is studied using the bulk method of X-ray topography. The topographs supplement the findings suggestive of modifications in the crystalline quality of SrFe12O19 on irradiation with SHI of Li3+. Etching of the (0001) cleaved surfaces in H3PO4 at 120°C suggests that the dissolution characteristics of the surfaces get affected on irradiation with SHI of Li3+, besides supporting the findings of HRXRD and X-ray topography regarding modifications in the perfection of SrFe12O19 on irradiation.
Volume 42 | Issue 5
Click here for Editorial Note on CAP Mode