    • Effect of chemical composition and alumina content on structure and properties of ceramic insulators

      Arman Sedghi Nastaran Riahi-Noori Naser Hamidnezhad Mohammad Reza Salmani

      More Details Abstract Fulltext PDF

      In the present work, six electrical porcelain compositions with different amount of alumina and silica have been prepared and fired in an industrial furnace at 1300°C. Density, porosity, bending strength and electrical strength were measured in the samples. In order to find a relationship between properties and sample microstructures, samples were analyzed by scanning electron microscope (SEM) and x-ray diffraction (XRD) techniques. The results showed that, with chemical composition of 53.5 wt.% SiO2 and 37.5 wt.% alumina, highest electrical strength of 21.97 kV/mm was achieved in fabricated electrical porcelains. Increasing amount of alumina up to 30 wt.% decreases quartz and cristobalite phases, but increases corundum phase 3 to 5 times. SEM observation revealed that dense particles and uniform distribution of long and thin needle shaped mullite are predominant in sample microstructures with highest electrical strength.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.