    • Wear and corrosion resistance of titanium carbo-nitride coated Al-7075 produced through PVD

      M K SRINATH M S GANESHA PRASAD

      More Details Abstract Fulltext PDF

      Titanium carbo-nitride coatings were deposited using plasma-assisted physical vapour deposition technique on Al-7075 aluminium alloy plates. Studies were conducted to understand the bonding between the coating and substrate, and to examine the wear- and corrosion-resistant properties under heat treatments. The nature of bonding was characterized using scanning electron microscope. The pin-on-disc wear test, according to G99 ASTM standard, displayed the frictional force, coefficient of friction and wear for the samples. Simultaneously, the corrosion tests, according to G5-14 ASTM standard,performed for a period of 48 h, using electrochemical impedance and potentiodynamic polarization tests displayed the Nyquist and Tafel plots for analysis. The wear and corrosion rates of samples heat-treated at 500$^{\circ}$C for 1 h were found tobe 0.066e-6 g s$^{−1}$ and 2.962e2 g mm$^{−2}$ s$^{−1}$, respectively. While that of samples heat-treated at 500$^{\circ}$C for 12 h were found to be 0.366e-6 g s$^{−1}$ and 4.177e2 g mm$^{−2}$ s$^{−1}$. Both the wear and the corrosion performance investigations were in goodagreement with each other. Thus, the tribo-corrosive deterioration of titanium carbo-nitride coated Al-7075 had escalated with an increase in durations of the heat treatment.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.