    • Properties of Nb-doped ZnO transparent conductive thin films deposited by rf magnetron sputtering using a high quality ceramic target

      J W Xu H Wang M H Jiang X Y Liu

      More Details Abstract Fulltext PDF

      Nb-doped ZnO films with (002) orientation have been grown on glass substrates by rf magnetron sputtering followed by vacuum annealing at 400°C for 3 h. The microstructures and surface figures of the Nbdoped ZnO films were investigated with X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. And its optical and electrical properties were measured at room temperature using a four-point probe technique and 756-type spectrophotometer, respectively. X-ray diffraction (XRD) revealed that the films are highly textured along the 𝑐 axis and perpendicular to the surface of the substrate. After annealing at 400°C for 180 min under vacuum, transmittance of about 90% in visible region for Nb doped ZnO films was confirmed by the optical transmission spectra, and the low resistivity of 5.47 × 10-3 𝛺.cm was obtained.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.