Volume 30 Issue 6 December 2007 pp 567-570 Ceramics and Glasses
Microwave synthesis and sintering characteristics of CaCu3Ti4O12
P Thomas L N Sathapathy K Dwarakanath K B R Varma
CaCu3Ti4O12 (CCTO) was synthesized and sintered by microwave processing at 2.45 GHz, 1.1 kW. The optimum calcination temperature using microwave heating was determined to be 950°C for 20 min to obtain cubic CCTO powders. The microwave processed powders were sintered to 94% density at 1000°C/60 min. The microstructural studies carried out on these ceramics revealed the grain size to be in the range 1–7 𝜇m. The dielectric constants for the microwave sintered (1000°C/60 min) ceramics were found to vary from 11000–7700 in the 100 Hz–100 kHz frequency range. Interestingly the dielectric loss had lower values than those sintered by conventional sintering routes and decreases with increase in frequency.
-
-
Bulletin of Materials Science
Volume 43, 2020
All articles
Continuous Article Publishing mode
-
Bulletin of Materials Science | News
-
Dr Shanti Swarup Bhatnagar for Science and Technology
Posted on October 12, 2020Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
Chemical Sciences 2020Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
Physical Sciences 2020 -
Editorial Note on Continuous Article Publication
Posted on July 25, 2019Click here for Editorial Note on CAP Mode
-