Volume 29 Issue 2 April 2006 pp 147-154 Alloys
Tensile behaviour of the near 𝛼 titanium alloy, Ti–6Al–5Zr–0.5Mo–0.25Si (LT26A), was investigated in (𝛼+𝛽) as well as 𝛽 treated condition, over a wide range of temperature from RT to 823 K. It was observed that there were distinct serrations on the load-elongation curves of the 𝛼 + 𝛽 treated material at intermediate temperatures from 623 to 723 K. Tensile tests at 673 K over a wide range of strain rate from 0.052 to 5.60 (× 10-2) s-1 showed negative strain rate sensitivity. Thus, occurrence of DSA was confirmed. It was established from the measured activation energy for DSA that it was essentially controlled by diffusion of the solid solution strengthener silicon in the matrix.
Volume 29 Issue 3 June 2006 pp 271-275 Alloys and Steels
Low cycle fatigue (LCF) behaviour of the near 𝛼 titanium alloy, Ti–6Al–5Zr–0.5Mo–0.25Si (LT26A), was investigated in the (𝛼 + 𝛽) as well as 𝛽 treated conditions at room temperature. LCF tests were carried out under total strain controlled mode in the range of 𝛥 𝜀t/2: from ± 0.60% to ± 1.40%. The alloy shows cyclic softening in both the conditions. Also it exhibits dual slope Coffin–Manson (C–M) relationship in both the treated conditions.
Volume 45, 2022
Continuous Article Publishing mode
Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
Chemical Sciences 2020
Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
Physical Sciences 2020
Click here for Editorial Note on CAP Mode