    • Application of mechano-chemical synthesis for protective coating on steel grinding media prior to ball milling of copper

      Indranil Lahiri K Balasubramanian

      More Details Abstract Fulltext PDF

      One of the major sources of contamination during mechanical milling/alloying is from the surface erosion of the container and the grinding medium. This can either be prevented by using grinding medium and container of same material of the milled material or by adding a coating of the milled material on them. The paper describes the observations made during a mechano-chemical reaction, being used for coating the balls and vials in a planetary ball mill. Visual observation, XRD, optical micrography and EDS analysis were used to understand the progress of the reaction. Copper was successfully coated on the steel balls and vials. The method can easily be adopted in daily production purposes, prior to mechanical milling of a Cu-based powder for prevention of Fe contamination.

    • High-temperature stability of yttria-stabilized zirconia thermal barrier coating on niobium alloy—C-103

      S S Panwar T Umasankar Patro K Balasubramanian B Venkataraman

      More Details Abstract Fulltext PDF

      Thermal barrier coatings (TBCs) of yttria-stabilized zirconia (YSZ) of different thicknesses with an intermediate bond coat were deposited on C-103 Nb alloy using the air plasma spraying technique. The coatings were subjected to rapid infra-red (IR) heating ($\sim$25°C s$^{−1}$) up to $\sim$1250°C and exposed up to 100 s at this temperature with heat flux varying from 55 to 61 Wcm$^{−2}$. The TBCs were found to be stable and intact after the heat treatment. In contrast, at the same conditions, the uncoated C-103 alloy specimen showed extensive oxidation followed by weight loss due to spallation. A maximum temperature drop of $\sim$200°C was observed on the opposite side of the coated alloy with 600 $\mu$m YSZ coat; as against negligible temperature drop in case of bare alloy specimen. The temperature drop was found to increase with the coating thickness of YSZ. The coatings before and after IR heating were investigated by scanning electron microscopy, X-ray diffraction, electron probe microanalysis, microhardness and residual stress measurements in order to understand the effect of thermal shock on the properties of the TBC. On account of these high-temperature properties, YSZ coating along with the bond coat is expected to find potential thermal barrier coating system on niobium alloys for supersonic vehicles.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.