In this paper, ternary NiFeW alloy coatings were prepared by jet electrodeposition, and the effects of lord salt concentration, jet speed, current density and temperature on the properties of the coatings, including the composition, microhardness, surface morphology, structure and corrosion resistance, were investigated. Results reveal that the depositionrate reaches a maximum value of 27.30 $\mu$m h$^{−1}$, and the total current efficiency is above 85%. The maximum microhardness is 605 HV, and the wear and corrosion resistance values of the alloy coating are good. Moreover, the ternary NiFeW alloy coating is smooth and bright, and it presents a dense cellular growth. The alloy plating is nanocrystalline and has face-centered cubic structure.