    • Effect of non-180° polarization invariants on the exchange bias of tetragonal ⟨001⟩ and rhombohedral ⟨111⟩ orientations of bismuth ferrite epitaxial thin films

      M M SAJMOHAN R RANJITH J A CHELVANE

      More Details Abstract Fulltext PDF

      BiFeO₃ (BFO) is the only room temperature multiferroic material that has been extensively studied due to its multifunctional properties. BFO with a canted G-type antiferromagnetic (AFM) ordering exhibits strong exchange bias characteristics with NiFe which offers the potential to design and utilize devices working based on multiferroic features. In the past, it was known that the presence of 180° domain walls of BFO hinders a plausible exchange bias interaction. To understand the role of the strain-induced effects on such 180° domain walls and its effect on the exchange bias, NiFe, a soft ferromagnetic layer, was grown on the epitaxial BFO AFM layers. An approximately 80 nm BFO layer was grown epitaxially in both the tetragonal (001) phase on the LaAlO₃ (001) substrate and the rhombohedral (111) phase on the SrTiO₃ (111) substrate, with a thin (10 nm) layer of Ni₈₀Fe₂₀ on top of it. An exchange bias of 510 Oe was observed in the tetragonal phase of BFO with a $c/a$ ratio of 1.22, which is comparable with the exchange bias shown by the (111) oriented rhombohedral phase (360 Oe). Both the tetragonal (001) and rhombohedral (111) layers possess ferroelectric polarization normal to the sample surface and so the domain walls are mostly 180° oriented which is expected to have a minimum effect on the exchange bias. However, the weak strain-induced structural variants in the (111) oriented rhombohedral BFO and the monoclinic distortion present in the tetragonal BFO introduce non-180° domain walls in the system. These variants arising due to the structural distortion are expected to play a key role in defining the ferroelectric domain wall nature, thereby exhibiting exchange bias characteristics.

  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.