Volume 36 Issue 2 April 2013 pp 265-270
Huabin Yang Xu Shan Changrong Zhou Qin Zhou Weizhou Li Jun Cheng
To improve the piezoelectric properties of Bi0.5Na0.5TiO3-based ceramics, a new perovskite-type leadfree piezoelectric (1 – 𝑥 – 𝑦)Bi0.5Na0.5TiO3−𝑥Bi0.5K0.5TiO3−𝑦BiMnO3 system has been fabricated by a conventional solid–state reaction method and their microstructure, dielectric and piezoelectric properties have been investigated. The results of X-ray diffraction (XRD) analysis reveal that the addition of small amounts of BiMnO3 did not cause a remarkable change in crystal structure, but resulted in an evident evolution inmicrostructure. An obvious secondary phase was observed in samples with high Bi0.5K0.5TiO3 content. It is found from dielectric constant curves that low-temperature hump disappeared with increasing y and it appeared again with increasing x. The piezoelectric properties significantly increase with increasing Bi0.5K0.5TiO3 and BiMnO3 content. The piezoelectric constant and electromechanical coupling factor attain maximum values of 𝑑33 = 182 pC/N at 𝑥 = 0.21(𝑦 = 0.01) and 𝑘p = 0.333 at 𝑥 = 0.18 (𝑦 = 0.01), respectively.
-
-
Bulletin of Materials Science
Volume 46, 2023
All articles
Continuous Article Publishing mode
-
Bulletin of Materials Science | News
-
Dr Shanti Swarup Bhatnagar for Science and Technology
Posted on October 12, 2020Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
Chemical Sciences 2020Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
Physical Sciences 2020 -
Editorial Note on Continuous Article Publication
Posted on July 25, 2019Click here for Editorial Note on CAP Mode
-