• Reduced-graphene-oxide-and-strontium-titanate-based double-layered composite: an efficient microwave-absorbing material

Microwave-absorbing materials based on reduced graphene oxide (r-GO)/ strontium titanate were prepared by embedding in epoxy matrix. R-GO and strontium titanate were synthesized and characterized before composite fabrication. Microstructures of the constituent elements were studied by scanning electron microscopy and X-ray diffraction (XRD). Microwave absorption capabilities of the composite absorbers were investigated using a Vector Network Analyser in the range 8–12 GHz. A maximum reflection loss of $−$7.5 and $−$16.4 dB was obtained at 9.3 and 12.08 GHz, respectively, for 2% (w/w) r-GO-loaded epoxy composites. A maximum attenuation of $−$12.8 dB at 9.3 GHz was obtained for the strontium titanate/epoxy composite. However, double-layer composite with r-GO/strontium titanate/epoxy composition showed the maximum reflection loss of $−$15.1 dB at 9.47 GHz and $−$9.65 dB at 12.3 GHz. All the results are discussed in terms of complex permeability and permittivity. The study revealed that intrinsic conductivity and polarization of the r-GO particles and dielectric polarization of the strontium titanate within epoxy matrix contribute to the microwave absorption.

• # Bulletin of Materials Science

Current Issue
Volume 42 | Issue 6
December 2019

• # Editorial Note on Continuous Article Publication

Posted on July 25, 2019