Volume 30 Issue 1 February 2007 pp 57-63 Electrochemistry
Polynitroaniline as brightener for zinc–nickel alloy plating from non-cyanide sulphate bath
H P Sachin Ganesha Achary Y Arthoba Naik T V Venkatesha
Electro-polymerization of orthonitroaniline was carried out on graphite electrode in hydrochloric acid medium. Zinc–nickel alloy deposition was carried out in the presence of polynitroaniline in acid sulphate bath. The bath constituent and bath variables were optimized through Hull cell experiments. The current efficiency and throwing power were measured. High shift of potential towards more cathodic direction was observed in presence of addition agent. Corrosion resistance test revealed good protection of base metal by zinc–nickel coating obtained from the developed electrolyte. SEM photomicrograph shows fine-grained deposit in the presence of addition agent. The consumption of brightener in the lab-scale was 0.01 gL-1 for 1000 amp-h.
Volume 30 Issue 3 June 2007 pp 219-224 Electrochemistry
Effect of a new condensation product on electrodeposition of zinc from a non-cyanide bath
Ganesha Achary H P Sachin Y Arthoba Naik T V Venkatesha
Zinc electrodeposition from sulphate chloride bath was carried out in presence of condensation product formed between chitosan and veratraldehyde. The bath constituents and operating parameters such as pH, temperature and current density were optimized through Hull cell experiments. Current efficiency and throwing power were measured. Polarization study revealed high shift of potential towards negative direction in the presence of addition agents. Corrosion resistance test revealed good protection of base metal by zinc coating obtained from developed electrolyte. SEM photomicrographs showed fine-grained deposit in the presence of condensation product. The IR spectrum of the deposit showed inclusion of the condensation product during electroplating. The consumption of brightener in the lab scale was 5 mLL-1 for 1000 amp-h.
Volume 46, 2023
Continuous Article Publishing mode
Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
Chemical Sciences 2020
Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
Physical Sciences 2020
Click here for Editorial Note on CAP Mode