    • Influence of carbon content on the microstructure, mechanical and tribological properties of CrAlCN coatings deposited by DC unbalanced magnetron sputtering

      ELBERT CONTRERAS ROMERO MARYORY GÓMEZ BOTERO WOLFGANG TILLMANN FRANCISCO BOLÍVAR OSORIO GILBERTO BEJARANO GAITÁN

      More Details Abstract Fulltext PDF

      The influence of carbon content on the microstructure, mechanical and tribological properties of CrAlCN was systematically investigated. For this purpose, five duplex coatings of CrAlCN deposited on AISI H13 steel by themagnetron-sputtering technique were developed. The carbon content of the coatingswas varied between 10.26 and 80.56 at% by modifying the percentage of methane in the working gas mixture CH$_4$/(Ar $+$ N$_2$). The effect of carbon content on the morphology, microstructure, mechanical and tribological properties of the CrAlCN coatingswas evaluated. Coatings showed a high crystalline structure at lowcarbon contents, consisting mainly of chromium nitrides and aluminium–chromium nitrides. With the increase of carbon content in the coatings, chromium carbides formed at the expense of nitrides, presenting a highly amorphous structure with high carbon content. Initially, the hardness and Young’s modulus of the coatings increased with carbon content, possibly due to hardening of the interstitial solid solution of carbon within the matrix of CrAlN. Then, they were decreased along with the coefficient of friction and wear rate due to the self-lubricating effect of graphite-like carbon. However, above the 54.74 at% carbon, the wear rate of CrAlCN increased again, probably due to the low hardness and adhesion of the coating. The CrAlCN coating with a carbon content of 21.96 at% presented the best balance between mechanical and tribological properties.

  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.