Volume 26 Issue 6 October 2003 pp 601-604 Alloys and Steels
This paper reports results of investigations carried out on a cast copper alloy containing 8 at.% Al. The alloy, and pure copper for the sake of comparison, were subjected to cold rolling with a final reduction of 30, 50 or 70%.
The cold rolled copper and copper alloy samples were isochronally and isothermally annealed up to the recrystallization temperature. The hardness, strength and electrical conductivity were measured and X-ray and DSC analyses performed.
Anneal hardening effect was observed in the alloy in the temperature range 180–300°C, followed by an increase in the electrical conductivity. The amount of strengthening increases with increasing degree of prior cold work. The X-ray analysis shows a change in the lattice parameter during annealing when anneal hardening effect was observed. The DSC analysis shows the exothermic character of this effect.
Volume 43, 2020
Continuous Article Publishing mode
Click here for Editorial Note on CAP Mode