    • The enhanced interface effect induced by thermal pressure in Nd0.7Sr0.3MnOy ceramics

      Shunsheng Chen Dawei Shi Shaozhen Li Changping Yang Yali Zhang

      More Details Abstract Fulltext PDF

      Polycrystalline ceramics Nd0.7Sr0.3MnOy prepared by solid-state reaction were treated under high pressure of 9 GPa and temperature of 1000 K. The electrical transport behaviour of samples were investigated by a variable temperature system and a peculiar transport character was found at low temperature of 120 K, the I–V showed an obvious step-shape behaviour with the increase in the measurement voltages; at much lower temperature of 12.3 K, the I–V curves exhibited a notable symmetric hysteresis at a critical voltage of 4.5 V, although a linear I–V behaviour at 293 K. On the other hand, the R–T measurement revealed that the resistivity peak (resistivity at 𝑇MI) disappeared gradually and is replaced by a resistivity platform with the increase in the load currents, surprisingly, the resistivity platform broadened with continuous increase in the load currents but weakened when an external magnetic field was applied. All of these phenomena were not observed for the un-treated sample. The particle attenuated and the enhanced interface effect which resulted from the violent thermal-pressure treatment was responsible for the unique electromagnetic transport.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.